张杰,王炯耿,周阳洋,胡洁梓,周宇通
ZHANG Jie,WANG Jionggen,ZHOU Yangyang,HU Jiezi,ZHOU Yutong

• 1:国网浙江省电力有限公司电力科学研究院
• 2:国网浙江省电力有限公司检修分公司

摘要(Abstract)：

针对某变电站一批145 k V隔离开关触头过热更换后再次发热的故障,采用宏观检查、X射线荧光镀银层测厚、金相分析、显微硬度分析、化学成分分析等方法,结合现场运行情况,分析触头发热的原因,得出该批触头发热的原因之一是其局部存在露铜、导致接触电阻升高,露铜是镀层的硬度不足引起耐磨性差所导致,并据此提出改进建议。
Contract overheat of 145 k V disconnectors reoccurred in a substation after replacement. Macroscopic examination, X-ray fluorescence silver plating layer thickness testing, metallographic analysis, microhardness analysis, chemical composition analysis methods are used to analysis the reasons by combining field operation. It is concluded that the contract heat comes from copper exposure due to poor abrasion resistance of the layer. This paper proposes some improvements.

关键词(KeyWords)： 隔离开关;触头;发热;金相分析;显微硬度分析;化学成分分析
disconnector;contact;overheat;metallographic analysis;microhardness analysis;chemical composition analysis

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 张杰,王炯耿,周阳洋,胡洁梓,周宇通
ZHANG Jie,WANG Jionggen,ZHOU Yangyang,HU Jiezi,ZHOU Yutong

DOI: 10.19585/j.zjdl.201805014

参考文献(References)：

• [1]王磊,严浩军,林钧,等.户外高压隔离开关电触头温升机理研究[J].广东电力,2014,27(12):92-96.
• [2]梁方建,张道乾.GW5-110型隔离开关触头发热缺陷分析及检修处理[J].高压电器,2008,44(1):89.
• [3]韦红军.GW5系列隔离开关触头发热原因分析及解决措施[J].设备管理与维护,2004(2):19.
• [4]带电设备红外诊断技术应用导则:DL/T 664-2008[S].北京:中国电力出版社,2008.
• [5]高压交流隔离开关和接地开关:DL/T 486-2010[S].北京:中国电力出版社,2010.
• [6]王富勇,方瑞明,陈华贵.户外高压隔离开关电触头发热及其在线监测[J].宁夏工程技术,2011(6):135.
• [7]赵庆,茅大钧.户外高压隔离开关触头发热机理分析及预防过热故障措施探讨[J].电气应用,2016,35(3):72.
• [8]张霁月,孙正来,卫功存,等.GW4型隔离开关触头发热原因分析及措施[J].安徽电气工程职业技术学院学报,2014,19(1):16-19.
• [9]詹鹏.解析隔离刀闸发热的原因及措施[J].能源电力,2016(2):67.
• [10]张丽英,董永杰,张涛.运行中的隔离开关触头发热原因分析与异常处理[J].中国新技术新产品,2008(11):98.
• [11]王富勇,陈华桂.基于电热场影响的户外隔离开关触头发热分析高压电器[J].2011,47(11):81.
• [12]许军,李坤.电接触的接触电阻研究[J].电工材料,2011(1):13.
• [13]王晓雷.承压类特种设备无损检测相关知识[M].北京:中国劳动社会保障出版社,2007.